  板狀剛玉
 
板狀剛玉0-0.5mm
【發表人:王青】【來源:板狀剛玉0-0.5mm】【發布時間:2019/4/19】

板狀剛玉具有良好的加熱體積溫度性和良好的抗熱震能力。其晶體呈平板狀交錯排列,增加了顆粒的機械強度;晶內和晶間以分布均勻的閉氣孔為主,體積密度高,顯氣孔和吸水率低,減少了再制品的用液量;具有高耐火度、良好的熱震穩定性、低熱收縮率和良好的熱負荷強度等優越的物理性能。同時,高純度避免了雜質對系統的污染,是制作高級耐火材料、陶瓷材料和絕緣材料的理想原料。

Tabular alumina has good heat resistance and good bulk temperature thermal shock capabilities. The crystal staggered plate shape, to increasing the mechanical strength of the particles; interior structure full of closed pores, high bulk density, low apparent porosity and water absorption, to reducing the amount of fluid re-use productions; With good physical properties like: high refractoriness, excellent thermal shock resistance, low shrinkage and good thermal load strength etc. Meanwhile, high-purity avoiding damage to machines. Hiaxu/Sicheng is your best choose as refractory material/ceramic material and insulating materials.

     

板狀剛玉是一種理想的耐火材料,既可以作為骨料應用于各種鋁質耐火材料中,也可以添加到其他鋁質不定型耐火材料中。

Application:

Tabular alumina is an ideal refractory material, either can be used in various refractory alumina, or can be add in other unshaped refractories

 

理化指標physical and chemical index

型號

Style

 

化學成分chemical index

物理指標 physical index

Al2O3%

SiO2%

Fe2O3%

Na2O%

體積密度

Volume density

吸水率

water absorption

顯氣孔率

apparent porosity

0-1mm

1-3mm

3-5mm

3-6mm

5-8mm

99.3

min

0.1

max

0.02

max

0.4

max

3.5g/cm3

1.5

5max

200#-0

320#-0

325#

99.1

min

0.15

max

0.04

max

0.4

max

3.45g/cm3

2.0

6max

 

 